การปรับปรุงสมบัติเชิงกลของวัสดุชีวภาพเชิงประกอบไฮดรอกซีแอปาไทต์–อะลูมินา ด้วยอนุภาคเซอร์โคเนีย
Main Article Content
Abstract
Abstract
In this work, the effect of ZrO2 additions on mechanical properties of HAp-Al2O3 based composite are investigated. HAp were mixed with 0, 20, 25 and 30 vol% Al2O3 to obtain various HAp-Al2O3 based composite Then (4Y)ZrO2 additive was mixed in the base composite with 0, 15, 20 and 25 vol% HAp-Al2O3/ ZrO2 composite were sintered at 1300, 1400 and1500oC. Density and phase of sintered composite were characterized. Flexural strength was also measured. As the result, the highest flexural strength was obtained from 20 vol% ZrO2 sintered at 1,500oC.