TREATMENT OF REACTIVE DYES IN AQUEOUS SOLUTION BY TIO2-PHOTOCATALYTIC DEGRADATION PROCESS

Authors

  • Kamonwan Limkhajonkiat Department of Environmental Science, Faculty of Environment, Kasetsart University
  • Kanita Tangkananurak Faculty of Environment, Kasetsart University

Keywords:

Photocatalytic degradation, TiO2, H2O2, Reactive dye

Abstract

 

         This research determine the efficiency of 3 reactive dyes (Red SBN, Blue G and Yellow RN) treatment by using photocatalytic degradation process. TiO2 thin film was prepared by the sol-gel method and coated on the surface of stainless steel sheet size 6.0×2.0×0.1 cm. The optimum condition for the 10 mg/L of each reactive dye solution were pH3, 6mM H2O2 and agitation 150 rpm at 180 min with UV black light lamp irradiation. The removal efficiency of Red SBN, Blue G and Yellow RN were 54.40%, 64.07% and 41.66% respectively. In addition, when reaction time was increased until 10 hr, 100% of removal efficiency of 3 reactive dyes were achieved. Furthermore, the mixed 3 reactive dyes solution was treated under the optimum condition, the color value of the treated solution was 212 ADMI that was lower than the industrial wastewater standard value (300 ADMI) Therefore, the TiO2 photocatalytic degradation process coupled with H2O2 had enough potential to treatment these 3 reactive dyes.

Downloads

Download data is not yet available.

References

Usa Chaijumnong. (2017, January- April). Treatment of Reactive Dyes in Wastewater from Native Textile House-Hold Factory by Using Constructed Filter Tank with Lignite Fly Ash Adsorbent. Thai Environmental Engineering Journal, 31(1), 45-57. Retrieved from https://www.tci-thaijo.org/index.php/teej/article/view/191731/133841

Kaoutar EI Hassani, Hajar Jabkhiro. (2019, August). Effect of drying step on layered double hydroxides properties: Application in reactive dye intercalation. Applied Clay Science, 182, 105246. Retrieved from https://portal.lib.ku.ac.th:10373/science/article/pii/S0169131719303047

Chandrakant R. Holkar, Ananda J. Jadhav, Dipak V. Pinjari. (2016, August). A critical review on textile wastewater treatments: Possible approaches. Journal of Environmental Management, 182, 351-366. Retrieved from https://portal.lib.ku.ac.th:10373/science/article/pii/S03014716305266

Siriphan Pruektara., & Paradee Chuaybamroong. (2018, April). Treatment of High Concentration Reactive Blue Dye with Fenton and Fenton-like Reactions Using Iron Filings. Thai Science and Technology Journal, 27(4), 661-674. Retrieved from https://www.tci-thaijo.org/index.php/tstj/article/view/189989/133069

Jaruwan Phanchomphu. (2015). Treatment of Textile Factory Wastewater by Using Lignite Fly Ash as Coagulant. Master of Science (Environmental Science). Bangkok: Graduate school of Kasetsart University.

Soutsas K, Karayanis V. (2009, October). Decolorization and degradation of reactive azo dyes via heterogeneous photocatalytic processes. Desalination, 250(1), 345-350. Retrieved October 20, 2012, from https://portal.lib.ku.ac.th:10373/science/article/pii/S0011916409010868

Pengwei Huo a, Yongsheng Yan. (2010, July). H2O2 modified surface of TiO2/fly-ash cenospheres and enhanced photocatalytic activity on methylene blue. Desalination, 263(1-3), 258-263. Retrieved October 20, 2012, from https://portal.lib.ku.ac.th:10373/science/article/pii/S0011916410004765

Sohrabi M. R., Ghavami M. (2009, November). Comparison of Direct Yellow 12 dye degradation efficiency using UV/semiconductor and UV/H2O2/semiconductor systems. Desalination, 252(1-3), 157-162. Retrieved October 20, 2012, from https://portal.lib.ku.ac.th:10373/science/article/pii/S0011916409012181

Siwimon Cheerprasert. (2015). Photocatalytic Reduction of Nitrate over Stainless Steel Coating with

Ag-TiO2. Master of Engineering (Environmental Engineering). Bangkok: Graduate school of Kasetsart University.

Krisana Kobwittaya. (2014). Photocatalytic Reduction of Nitrate over TiO2 and Metal-Modified TiO2. Master of Engineering (Environmental Engineering). Bangkok: Graduate school of Kasetsart University.

Hathaisamit K., Sutha W., Kamruang P., Pudwat S., Teekasap S. (2012, November). Decolorization of Cationic Yellow X-Gl 200% from Textile Dyes by TiO2 Films-Coated Rotor. Procedia Engineering, 32, 800-806. Retrieved October 20, 2012, from https://www.sciencedirect.com/science/article/pii/S1877705812014397

Emad S Elmolla. (2009, November). Photocatalytic degradation of amoxicillin, ampicillin and cloxacillin antibiotics in aqueous solution using UV/TiO2 and UV/H2O2/TiO2 photocatalysis. Desalination, 252(1-3), 46-52. Retrieved October 21, 2012, from https://portal.lib.ku.ac.th :10373/science/article/pill/S001191640902788

Department of industrial works. (2017). Industrial wastewater standard value. Bangkok. Retrieved from http://www.diw.go.th/hawk/news/11.PDF

Adly M. S., EI-Dafrawy Sh M. (2019, September). Application of nanostructured graphene oxide/titanium dioxide composites for photocatalytic degradation of rhodamine B and acid green 25 dyes. Journal of Materials Research and Technology. Retrieved from https://portal.lib.ku.ac.th: 10373/science/article/pii/S2238785419303977

Downloads

Published

2021-06-30

How to Cite

Limkhajonkiat, K. ., & Tangkananurak, K. . (2021). TREATMENT OF REACTIVE DYES IN AQUEOUS SOLUTION BY TIO2-PHOTOCATALYTIC DEGRADATION PROCESS. Srinakharinwirot University Journal of Sciences and Technology, 13(25, January-June), 1–12. Retrieved from https://ph02.tci-thaijo.org/index.php/swujournal/article/view/246628