Fe-16Cr-2Mo ที่มีการเติมซิลิคอน Influence of Welding Sequence on the Hardness of High Chromium Cast Iron Fe-16Cr-2Mo adding Silicon
Keywords:
high chromium cast iron, hard facing welding, welding layerAbstract
The objective of this research was to study the welding layer on hardness properties of high chromium cast iron with silicon additions of 0.5%, 1%, 1.5%, and 2%, aiming to provide guidelines for hard facing welding of workpieces susceptible to wear. Specimens were annealed at 950 degrees celsius for 1 hour and then welded in four patterns using MG 750 W and 450 R welding wires. Subsequently, hardness tests were conducted using a Vickers hardness tester, and microstructural examination. Experimental results revealed that single and double-layer
welds using 450R welding wire exhibited higher hardness values with the presence of carbides M7C3 and M23C6 compared to welds using MG 750W wire, where predominantly M23C6 carbides were found. Double-layer welding resulted in higher hardness values in the HAZ region compared to single-layer welding due to repeated heating from welding compared to the tempering process, which promoted the precipitation of secondary carbides in the matrix. Regarding the material type according to the silicon content, an increase in hardness was observed in specimens with 0.5-1.5% silicon additions, while hardness decreased when the silicon content increased to 2%, both in the welded metal and base metal regions.
References
Gucwa M, Bęczkowski R, Winczek J, Wyleciał T. The Effect of Type of Welding Sequence During Hardfacing Chromium Cast Iron for Erosion Resistance . Archives of foundry Engineering .2017; 17(3): 51-54.
Kosasu P, Inthidech S, Srichareonchai P Yasuhiro M. Effect of Silicon on Subcritical Heat Treatment Behavior and Wear Resistance of 16 wt% Cr Cast Iron with 2 wt% Mo. Journal of Metals, Materials and Minerals. 2012;22(2):89-95.
Mician M, Konar R, Hlavaty I. Winczek J, M. Gucwa The Repair of Foundry Defects in Steel Castings Using Welding Technology .Archives of foundry Engineering .2018; 18(2): 177-180.
Xinghui L, Welding Repair of High Chromium Cast Iron Defects. Key Engineering Materials .2019;814:229-232.
ทวี หมัดส๊ะ, ปิยะวรรณ สูนาสวนม, อรจิตร แจ่มแสง. การศึกษาความสัมพันธ์ระหว่างตัวแปรการเชื่อมอาร์กโลหะแก๊สคลุมและ สมบัติของโลหะเชื่อมพอกแข็งเหล็กหล่อสีเทา. วารสารวิศวกรรมศาสตร์ ราชมงคลธัญบุรี 2019;17(1) :103-113.
กิตติพงษ์ กิมะพงศ์, สุรัตน์ ตรัยวนพงศ์, สุริยา ประสมทอง และคณะ. อิทธิพลของการรองพื้นและการพอกผิวแข็งต่อสมบัติทางกล ของโลหะเชื่อมเหล็กกล้าคาร์บอน JIS-S50C. วารสารวิศวกรรมศาสตร์ ราชมงคลธัญบุรี. 2016; 14(1): 77-86.
American Welding Society. Welding Handbook Ninth Edition Volume 4 material and application, Part 1. Miami: Printed in the United States of America; 2011.
H. Wang and S. Yu Influence of heat treatment on microstructure and sliding wear resistance of high chromium cast iron electroslag hardfacing layer.Surface & Coatings Technology.2017;319:182–190.
Zixiang L , Yinan C , Jie W, et al. Characterization of Microstructure and Mechanical Properties of Stellite 6 Part Fabricated by Wire Arc Additive Manufacturing. Metals. 2019: 9:474.
Wieczerzak k, Bała p, Stępien m, et al. The characterization of cast Fe-Cr-C alloy charakterystyka stopu Fe-Cr-C W stanie lanym archives of metallurgy and materials. 2015; 60: 779-782.
Kosasu P , Inthidech S Effect of Silicon on Abrasive Wear Behavior of Heat-Treated 16% Cr - 2% Mo Cast Iron RMUTI JOURNAL Science and Technology.2019; 12 (1):42-56.
Inthidech S, Boonmak K, Sricharoenchai P, et al. Effect of Repeated Tempering on Hardness and Retained Austenite of High Chromium Cast Iron Containing Molybdenum Materials Transactions. 2010; 51(7): 1264- 127
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 UTK RESEARCH JOURNAL
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
กองบรรณาธิการวารสารวิชาการ มหาวิทยาลัยเทคโนโลยีราชมงคลกรุงเทพ มีความยินดีที่จะรับบทความจากอาจารย์ นักวิจัย นักวิชาการทั้งภายในและภายนอกมหาวิทยาลัย ในสาขาวิชาวิทยาศาสตร์และเทคโนโลยี ได้แก่ สาขาวิชาวิทยาศาสตร์ วิศวกรรมศาสตร์ และสาขาอื่นๆ ที่เกี่ยวข้อง รวมถึงสาขาต่างๆ ที่มีการบูรณาการข้ามศาสตร์ที่เกี่ยวข้องวิทยาศาสตร์และเทคโนโลยี ที่เขียนเป็นภาษาไทยหรือภาษาอังกฤษ ซึ่งผลงานวิชาการที่ส่งมาขอตีพิมพ์ต้องไม่เคยเผยแพร่ในสิ่งพิมพ์อื่นใดมาก่อน และต้องไม่อยู่ในระหว่างการพิจารณาของวารสารอื่น
การละเมิดลิขสิทธิ์ถือเป็นความรับผิดชอบของผู้ส่งบทความโดยตรง บทความที่ได้รับการตีพิมพ์ต้องผ่านการพิจารณากลั่นกรองคุณภาพจากผู้ทรงคุณวุฒิและได้รับความเห็นชอบจากกองบรรณาธิการ
ข้อความที่ปรากฏอยู่ในแต่ละบทความที่ตีพิมพ์ในวารสารวิชาการเล่มนี้ เป็นความคิดเห็นส่วนตัวของผู้เขียนแต่ละท่าน ไม่เกี่ยวข้องกับมหาวิทยาลัยเทคโนโลยีราชมงคลกรุงเทพแต่อย่างใด ความรับผิดชอบด้านเนื้อหาและการตรวจร่างบทความแต่ละบทความเป็นของผู้เขียนแต่ละท่าน หากมีความผิดพลาดใดๆ ผู้เขียนแต่ละท่านจะต้องรับผิดชอบบทความของตนเองแต่ผู้เดียว
กองบรรณาธิการขอสงวนสิทธิ์มิให้นำเนื้อหา หรือข้อคิดเห็นใดๆ ของบทความในวารสารวิชาการ มหาวิทยาลัยเทคโนโลยีราชมงคลกรุงเทพ ไปเผยแพร่ก่อนได้รับอนุญาตจากกองบรรณาธิการ อย่างเป็นลายลักษณ์อักษร ผลงานที่ได้รับการตีพิมพ์ถือเป็นลิขสิทธิ์ของวารสาร